Multilayer Zirconia
Multilayer zirconia disk
ThridenTM zirconia block Compositions: ZrO2(92%-99%), Y2O3(4.5%-9.7%), AL2O3(0.2%-0.5%), other Oxides (<0.5%) block, which is made from the finest nanometer zirconia powder by dry and cold isostatic pressing and machining.
Technical Facts | ST ML | SHT ML | UT ML |
Post-sintering Flexural Strength | 1200Mpa | 900Mpa | 600Mpa |
Translucent | 43% | 46% | 49% |
Sintering temperature | 1480°C | 1480°C | 1480°C |
Available size, color and system:
System | Thickness and color |
Open CADCAM system (for Roland, VHF, Imes-icores, Yenadent, Wieland, Dentium, Chinese Brand and so on.) | 10mm-30mm; A1 A2 A3 A3.5 A4 / B1 B2 B3 B4 / C1 C2 C3 C4 / D2 D3 D4 / BL1 BL2 BL3 BL4
|
Amann Girrbach system | |
Zirkonzahn system |
Our advantages:
1. Raw material: we have established in-depth cooperation with many medical-grade nanometer zirconia powder manufacturers at home
abroad and insist on using the finest Nano zirconia powder all the time.
2. Production technology: we adopt isostatic pressing, slurry forming, SPS and so on to ensure the advanced performance of our products, and
we always keep in touch with many leading’s researching organizations to continually update our processes.
3. Support and service: we provide detailed product parameters and various guidance to help to make the best zirconia denture.
4. Quality control: we strictly insist on ISO quality system, make it as part of our manufacturing operation.With highly precise measuring
equipment, we can assures the ultimate consistency in quality.